Шаблон:Short description 440C (UNS designation S44004) is a martensitic 400 series stainless steel,[1] and has the highest carbon content of the 400 stainless steel series. It can be heat treated to reach hardness of 58 to 60 HRC. It can be used to make rolling contact stainless bearings, e.g. ball bearings and roller bearings. It is also used to make knife blades.

440C has the highest strength, hardness, and wear resistance of all the commonplace 440-series stainless alloys, with high carbon content and moderate corrosion resistance.[2]

Composition

Chemical Composition (wt%)[1][3]
C Cr Mn Si Mo P S Fe
0.95-1.20 16.0-18.0 1.00 1.00 0.75 0.040 0.030 Balance

Mechanical properties

Typical Mechanical Properties as a Bar [4]
Heat Treatment Young's Modulus (GPa) 0.2% Offset Yield Strength (MPa) Tensile Strength (MPa) Elongation (%) Rockwell Hardness CTE (0-100 °C)

(µm/m)

Thermal Conductivity (at 100 °C) (W/m*K)
Annealed 200 425 760 14 97 HRB 10.2 24.2
Tempered at 315 °C 200 1900 1970 2 57 HRC 10.2 24.2