Шаблон:Short description The alkali–carbonate reaction is an alteration process first suspected in the 1950s in Canada for the degradation of concrete containing dolomite aggregates.[1][2]
Alkali from the cement might react with the dolomite crystals present in the aggregate inducing the production of brucite, (MgOH)2, and calcite (CaCO3). This mechanism was tentatively proposed by Swenson and Gillott (1964)[3] and may be written as follows:
- <chem>CaMg(CO3)2 + 2 NaOH -> Mg(OH)2 + CaCO3 + Na2CO3</chem>
Brucite (Mg(OH)2), could be responsible for the volumetric expansion after de-dolomitisation of the aggregates, due to absorption of water.
The alkali–carbonate reaction is also catalyzed by the soluble NaOH produced by the reaction of Шаблон:Chem with Шаблон:Chem (portlandite) present in the hardened cement paste (HCP), therefore perpetuating the reaction indefinitely as observed by Fournier and Bérubé (2000) and Bérubé et al. (2005).[4][5]
- <chem>Na2CO3 + Ca(OH)2 -> CaCO3 + 2 NaOH</chem>
The sum of the two above mentioned reactions leading to the ultimate production of brucite and calcium carbonate can be written as follows:
- <chem>CaMg(CO3)2 + Ca(OH)2 -> Mg(OH)2 + 2 CaCO3</chem>
The alkali-carbonate reaction is much less understood than the alkali-silica reaction. Both reactions share in common the continuous regeneration of the sodium hydroxide (NaOH) after the reaction of soluble sodium carbonate or sodium silicate with calcium hydroxide, Шаблон:Chem. However, impure dolomitic aggregates also often contain clay impurities, and small amounts of pyrite (Шаблон:Chem) and organic matter. The alkali-carbonate reaction could therefore also simply hide an alkali-silica or an alkali-silicate reaction. Anyway a chemical coupling between ACR and ASR cannot be ruled out.
See also
- Alkali–aggregate reaction
- Alkali–silica reaction
- Calthemite: Secondary calcium carbonate deposit growing under man-made structures
- Pozzolanic reaction
External links
References
- ↑ Swenson, E.G. (1957a) A reactive aggregate undetected by ASTM test. ASTM Bulletin, 226: 48–50.
- ↑ Swenson, E.G. (1957b) Cement-aggregate reaction in concrete of a Canadian bridge. ASTM Proceedings, 57: 1043–1056.
- ↑ Шаблон:Cite journal
- ↑ Шаблон:Cite journal
- ↑ Bérubé, M. A., Smaoui, N., Bissonnette, B., & Fournier, B. (2005). Outil d’évaluation et de gestion des ouvrages d’art affectés de réactions alcalis-silice (RAS). Études et Recherches en Transport, Ministère des Transports du Québec. See the chemical equations on pp. 3-4.
- Английская Википедия
- Building materials
- Carbonates
- Catalysis
- Cement
- Chemical reactions
- Concrete
- Fracture mechanics
- Magnesium compounds
- Materials degradation
- Mechanical failure modes
- Patterns
- Pavements
- Silicates
- Страницы, где используется шаблон "Навигационная таблица/Телепорт"
- Страницы с телепортом
- Википедия
- Статья из Википедии
- Статья из Английской Википедии