Bismuth(III) oxide is perhaps the most industrially important compound of bismuth. It is also a common starting point for bismuth chemistry. It is found naturally as the mineral bismite (monoclinic) and sphaerobismoite (tetragonal, much more rare), but it is usually obtained as a by-product of the smelting of copper and lead ores. Dibismuth trioxide is commonly used to produce the "Dragon's eggs" effect in fireworks, as a replacement of red lead.

Structure

The structures adopted by Шаблон:Chem2 differ substantially from those of arsenic(III) oxide, Шаблон:Chem2, and antimony(III) oxide, Шаблон:Chem2.

Файл:Bi2O3 phases.svg

Existence domains of the four polymorphs of Шаблон:Chem2 as a function of temperature. (a) The α-phase transforms to the δ-phase when heated above 727 °C, which remains the structure until the melting point, 824 °C, is reached. When cooled, the δ-phase transforms into either the β-phase at 650 °C, shown in (b), or the γ-phase at 639 °C, shown in (c). The β-phase transforms to the α-phase at 303 °C. The γ-phase may persist to room temperature when the cooling rate is very slow, otherwise it transforms to the α-phase at 500 °C.

Bismuth oxide, Шаблон:Chem2 has five crystallographic polymorphs. The room temperature phase, α-Шаблон:Chem2 has a monoclinic crystal structure. There are three high temperature phases, a tetragonal β-phase, a body-centred cubic γ-phase, a cubic δ-Шаблон:Chem2 phase and an ε-phase. The room temperature α-phase has a complex structure with layers of oxygen atoms with layers of bismuth atoms between them. The bismuth atoms are in two different environments which can be described as distorted 6 and 5 coordinate respectively.

β-Шаблон:Chem2 has a structure related to fluorite.

γ-Шаблон:Chem2 has a structure related to that of sillenite (Шаблон:Chem2), but in which a small fraction of the bismuth atoms occupy positions occupied by silicon atoms in sillenite, so the formula may be written as Шаблон:Chem2. The crystals are chiral (space group I23, or no. 197) with two Шаблон:Chem2 formulas per unit cell.

δ-Шаблон:Chem2 has a defective fluorite-type crystal structure in which two of the eight oxygen sites in the unit cell are vacant. ε-Шаблон:Chem2 has a structure related to the α- and β- phases but as the structure is fully ordered it is an ionic insulator. It can be prepared by hydrothermal means and transforms to the α- phase at 400 °C.

The monoclinic α-phase transforms to the cubic δ-Шаблон:Chem2 when heated above 729 °C, which remains the structure until the melting point, 824 °C, is reached. The behaviour of Шаблон:Chem2 on cooling from the δ-phase is more complex, with the possible formation of two intermediate metastable phases; the tetragonal β-phase or the body-centred cubic γ-phase. The γ-phase can exist at room temperature with very slow cooling rates, but α-Шаблон:Chem2 always forms on cooling the β-phase. Even though when formed by heat, it reverts to α-Шаблон:Chem2 when the temperature drops back below 727 °C, δ-Шаблон:Chem2 can be formed directly through electrodeposition and remain relatively stable at room temperature, in an electrolyte of bismuth compounds that is also rich in sodium or potassium hydroxide so as to have a pH near 14.

Conductivity

The α-phase exhibits p-type electronic conductivity (the charge is carried by positive holes) at room temperature which transforms to n-type conductivity (charge is carried by electrons) between 550 °C and 650 °C, depending on the oxygen partial pressure. The conductivity in the β, γ and δ-phases is predominantly ionic with oxide ions being the main charge carrier. Of these δ-Шаблон:Chem2 has the highest reported conductivity. At 750 °C the conductivity of δ-Шаблон:Chem2 is typically about 1 S cm⁻¹, about three orders of magnitude greater than the intermediate phases and four orders greater than the monoclinic phase. δ-Шаблон:Chem2 has a defective fluorite-type crystal structure in which two of the eight oxygen sites in the unit cell are vacant. These intrinsic vacancies are highly mobile due to the high polarisability of the cation sub-lattice with the 6s² lone pair electrons of Шаблон:Chem2. The Bi–O bonds have covalent bond character and are therefore weaker than purely ionic bonds, so the oxygen ions can jump into vacancies more freely.

The arrangement of oxygen atoms within the unit cell of δ-Шаблон:Chem2 has been the subject of much debate in the past. Three different models have been proposed. Sillén (1937) used powder X-ray diffraction on quenched samples and reported the structure of Шаблон:Chem2 was a simple cubic phase with oxygen vacancies ordered along <111>, the cube body diagonal. Gattow and Schroder (1962) rejected this model, preferring to describe each oxygen site (8c site) in the unit cell as having 75% occupancy. In other words, the six oxygen atoms are randomly distributed over the eight possible oxygen sites in the unit cell. Currently, most experts seem to favour the latter description as a completely disordered oxygen sub-lattice accounts for the high conductivity in a better way.

Willis (1965) used neutron diffraction to study the fluorite (Шаблон:Chem2) system. He determined that it could not be described by the ideal fluorite crystal structure, rather, the fluorine atoms were displaced from regular 8c positions towards the centres of the interstitial positions. Shuk et al. (1996) and Sammes et al. (1999) suggest that because of the high degree of disorder in δ-Шаблон:Chem2, the Willis model could also be used to describe its structure.

Use in solid-oxide fuel cells (SOFCs)

Interest has centred on δ-Шаблон:Chem2 as it is principally an ionic conductor. In addition to electrical properties, thermal expansion properties are very important when considering possible applications for solid electrolytes. High thermal expansion coefficients represent large dimensional variations under heating and cooling, which would limit the performance of an electrolyte. The transition from the high-temperature δ-Шаблон:Chem2 to the intermediate β-Шаблон:Chem2 is accompanied by a large volume change and consequently, a deterioration of the mechanical properties of the material. This, combined with the very narrow stability range of the δ-phase (727–824 °C), has led to studies on its stabilization to room temperature.

Шаблон:Chem2 easily forms solid solutions with many other metal oxides. These doped systems exhibit a complex array of structures and properties dependent on the type of dopant, the dopant concentration and the thermal history of the sample. The most widely studied systems are those involving rare earth metal oxides, Шаблон:Chem2, including yttria, Шаблон:Chem2. Rare earth metal cations are generally very stable, have similar chemical properties to one another and are similar in size to Шаблон:Chem2, which has a radius of 1.03 Å, making them all excellent dopants. Furthermore, their ionic radii decrease fairly uniformly from Шаблон:Chem2 (1.032 Å), through Шаблон:Chem2 (0.983 Å), Шаблон:Chem2 (0.938 Å), Шаблон:Chem2 (0.912 Å) and Шаблон:Chem2 (0.89 Å), to Шаблон:Chem2 (0.861 Å) (known as the "lanthanide contraction"), making them useful to study the effect of dopant size on the stability of the Шаблон:Chem2 phases.

Шаблон:Chem2 has also been used as sintering additive in the Шаблон:Chem2-doped zirconia system for intermediate temperature SOFC.

Preparation

The trioxide can be prepared by ignition of bismuth hydroxide. Bismuth trioxide can be also obtained by heating bismuth subcarbonate at approximately 400 °C.

Reactions

Atmospheric carbon dioxide or Шаблон:Chem2 dissolved in water readily reacts with Шаблон:Chem2 to generate bismuth subcarbonate. Bismuth oxide is considered a basic oxide, which explains the high reactivity with Шаблон:Chem2. However, when acidic cations such as Si(IV) are introduced within the structure of the bismuth oxide, the reaction with Шаблон:Chem2 do not occur.

Bismuth(III) oxide reacts with a mixture of concentrated aqueous sodium hydroxide and bromine or aqueous potassium hydroxide and bromine to form sodium bismuthate or potassium bismuthate, respectively.

Usage

Medical devices

Bismuth oxide is occasionally used in dental materials to make them more opaque to X-rays than the surrounding tooth structure. In particular, bismuth (III) oxide has been used in hydraulic silicate cements (HSC), originally in "MTA" (a trade name, standing for the chemically-meaningless "mineral trioxide aggregate") from 10 to 20% by mass with a mixture of mainly di- and tri-calcium silicate powders. Such HSC is used for dental treatments such as: apicoectomy, apexification, pulp capping, pulpotomy, pulp regeneration, internal repair of iatrogenic perforations, repair of resorption perforations, root canal sealing and obturation. MTA sets into a hard filling material when mixed with water. Some resin-based materials also include an HSC with bismuth oxide. Problems have allegedly arisen with bismuth oxide because it is claimed not to be inert at high pH, specifically that it slows the setting of the HSC, but also over time can lose color by exposure to light or reaction with other materials that may have been used in the tooth treatment, such as sodium hypochlorite.

Radiative cooling

Bismuth oxide was used to develop a scalable colored surface high in solar reflectance and heat emissivity for passive radiative cooling. The paint was non-toxic and demonstrated a reflectance of 99% and emittance of 97%. In field tests the coating exhibited significant cooling power and reflected potential for the further development of colored surfaces practical for large-scale radiative cooling applications.

Further reading